Tensile Strength, min |
|
Yield Strength (0.2%Offset) min or range |
|
Elongation in 4D |
Reduction of Area |
Grade |
ksi |
Mpa |
ksi |
Mpa |
min.% |
min.% |
1 |
35 |
240 |
20 |
138 |
24 |
30 |
2 |
50 |
345 |
40 |
275 |
20 |
30 |
2H |
58 |
400 |
40 |
275 |
20 |
30 |
3 |
65 |
450 |
55 |
380 |
18 |
30 |
4 |
80 |
550 |
70 |
483 |
15 |
25 |
5 |
130 |
895 |
120 |
828 |
10 |
25 |
6 |
120 |
828 |
115 |
795 |
10 |
25 |
7 |
50 |
345 |
40 |
275 |
20 |
30 |
7H |
58 |
400 |
40 |
275 |
20 |
30 |
9 |
90 |
620 |
70 |
483 |
15 |
25 |
9i |
90 |
620 |
70 |
483 |
12 |
25 |
11 |
35 |
240 |
20 |
138 |
24 |
30 |
12 |
70 |
483 |
50 |
345 |
18 |
25 |
13 |
40 |
275 |
25 |
170 |
24 |
30 |
14 |
60 |
410 |
40 |
275 |
20 |
30 |
15 |
70 |
483 |
55 |
380 |
18 |
25 |
16 |
50 |
345 |
40 |
275 |
20 |
30 |
16H |
58 |
400 |
40 |
275 |
20 |
30 |
17 |
35 |
240 |
25 |
170 |
24 |
30 |
18 |
90 |
620 |
70 |
483 |
15 |
25 |
18i |
90 |
620 |
70 |
483 |
12 |
20 |
19ii |
115 |
793 |
110 |
759 |
15 |
25 |
19iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
19E |
165 |
1138 |
160 to 185 |
1104 to 1276 |
5 |
20 |
20ii |
115 |
793 |
110 |
759 |
15 |
25 |
20iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
20iv |
165 |
1138 |
160 to 185 |
1104 to1276 |
5 |
20 |
21ii |
115 |
793 |
110 |
759 |
15 |
35 |
21iii |
140 |
966 |
130 to 159 |
897 to 1096 |
10 |
30 |
21iv |
170 |
1172 |
160 to 185 |
1104 to 1276 |
8 |
20 |
23 |
120 |
828 |
110 |
759 |
10 |
15 |
23i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
25 |
24 |
130 |
895 |
120 |
828 |
10 |
25 |
25 |
130 |
895 |
120 |
828 |
10 |
25 |
26 |
50 |
345 |
40 |
275 |
20 |
30 |
27 |
35 |
240 |
25 |
170 |
24 |
30 |
28 |
90 |
620 |
70 |
483 |
15 |
25 |
28i |
90 |
620 |
70 |
483 |
12 |
20 |
29 |
120 |
828 |
110 |
759 |
10 |
25 |
29i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
15 |
30 |
50 |
345 |
40 |
275 |
20 |
30 |
31 |
65 |
450 |
55 |
380 |
18 |
30 |
32 |
100 |
689 |
85 |
586 |
10 |
25 |
33 |
50 |
345 |
40 |
275 |
20 |
30 |
34 |
65 |
450 |
55 |
380 |
18 |
30 |
35 |
130 |
895 |
120 |
828 |
5 |
20 |
36 |
65 |
450 |
60 to 95 |
410 to 655 |
10 |
|
37 |
50 |
345 |
31 |
215 |
20 |
30 |
38 |
130 |
895 |
115 |
794 |
10 |
25 |
Above properties apply to longitudinal sections up to 3 inch thickness with maximum of 10 inch. Mechanical properties of larger sections shall be negotiated between the manufacturer and purchaser. |
||||||
i) Properties for material in transformed-beta condition. |
||||||
ii) Properties for solution treated condition. |
||||||
iii) Properties for solution treated and aged condition-Moderate strength (determined by aging temperature). |
||||||
iv) Properties for solution treated and aged condition-High strength (determined by aging temperature). |
||||||
v) For product section or wall thickness values < 1.0 in. |
||||||
vi) For product section or wall thickness values_> 1.0 in. | ||||||
**While this information has been compiled with care, it is for convenience and for reference only and we assume no liability for any decisions based on the content therein. It shall be your responsibility to ensure that any information in this document or on our website meets your specific requirements.** |